| Hot-Dip Aluminium-Zinc Alloy Coated Steel |
The product is characterized by stronger corrosion resistance than hot-dip galvanized steel. It also provides excellent heat resistance and heat reflection property that Hot-dip Galvanized Steel cannot compare with.
 |
Manufacturing
Parts in oven and toaster, transformer case, air conditioner part, motor case, oven, exhausted system, refrigerator black plate, |
|
Construction
Air-duct, ceiling, wall partition, roofing |
|
| Specification |
| JIS G 3321 ??Hot-Dip Aluminium-Zinc Alloy Coated Steel |
Grade and symbol (for hot-rolled based metal used)
| Classified symbol |
Application |
| SGLHC |
Commercial quality |
| SGLH400 |
Structural quality |
| SGLH440 |
| SGLH490 |
| SGLH540 |
Grade and symbol (for cold-rolled based metal used)
| Classified symbol |
Application |
| SGLCC |
Commercial quality |
| SGLCD |
Drawing quality |
| SGLC400 |
Structural quality |
| SGLC440 |
| SGLC490 |
| SGLC570 |
Minimum coating mass for equally coated sheet and coil (total mass on both surfaces, unit: g/m²)
| Coating mass symbol |
Average coating mass in triple-spot test |
Minimum coating mass at a single spot |
| AZ90 |
90 |
76 |
| AZ120 |
120 |
102 |
| AZ150 |
150 |
130 |
| AZ170 |
170 |
145 |
Tensile strength and yield point (for hot-rolled base metal used)
| Classified symbol |
Tensile strength
N/mm² |
Yield point
N/mm² |
| SGLHC |
270 min. |
205 min. |
| SGLH400 |
400 min. |
295 min. |
| SGLH440 |
440 min. |
* |
| SGLH490 |
490 min. |
365 min. |
| SGLH540 |
540 min. |
* |
* The value shall be agreed between the purchaser and manufacturer
Tensile strength and yield point (for cold-rolled base metal used)
| Classified symbol |
Tensile strength
N/mm² |
Yield point
N/mm² |
| SGLCC |
270 min. |
205 min. |
| SGLCD |
270 min. |
--- |
| SGLC440 |
400 min. |
295 min. |
| SGLC440 |
440 min. |
335 min. |
| SGLC490 |
490 min. |
365 min. |
| SGLC570 |
570 min. |
560 min. |
* The value shall be agreed between the purchaser and manufacturer |